Catalytic ceramic plate for infrared ceramic plate combustion

Infrared ceramic plate made from high purity cordierite material and other components, it is widely used as the burner media in aplliance such as gas burner, oven, grill BBQ, heater, rue biscuit, smokeless oven etc. This product has good thermal shock resistance ( no cracks on the product

Featured Products

Infrared ceramic plate made from high purity cordierite material and other components, it is widely used as the burner media in aplliance such as gas burner, oven, grill BBQ, heater, rue biscuit, smokeless oven etc. This product has good thermal shock resistance ( no cracks on the product if the honeycomb ceramic with 1000 is in the water with 20 for 3 times ), high mechanical strength ( crushing strength is 20MPa on the top and 5MPa on the side), good endurance for high temperature, high resistance for erosion.

Honeycomb ceramics Balanced distribution heat, promote the complete combustion, over 10% of energy can be save. Larger specific surface area, fluid distribution uniformity, high separation efficiencyhas, it has high surfarce area, low air flow resistance. Catalyst carrier it can clean waste gas. We can also provide coating for infrared ceramic plate to raise the surface temperature and reduce the exhaust emission.

Gas Hot burning infrared ceramic plate Application:
*Stove
*Gas water heater
*Burn oven
*Industrial baking equipment
*Industrial organic waste gas combustion

Physical Merits:
*Good thermal shock resistance ( no cracks after 3 times thermal shock from 800 ° C to cold water),
*High mechanical strength ( crushing strength is 20MPa on the top and 5MPa on the side),
*Good endurance for high temperature
*High resistance for erosion

Advantages:
*20%-50% energy saving
*Mixes oxygen completely with the gas, burning efficiently with no flame and little noise
*Operating safety without being influenced by wind when operating outdoor
*Decreasing the CO and NOx poisonous gas disposal and remove harmful

Chemical compositionContentChemical compositionContent
Al 2 O 320-85Acid resistance %≥ 99.8%
SiO 2  + Al 2 O 392Alkali resistance %≥ 86%
Fe 2 O 3<0.8Refractoriness  ° C≥ 1200 ° C
Out porous ratio7.0-10%Thermal stabilityNo crack after three times

Specification
mm
Fuel gasholeCells/In 2 (CPSI)suuface
NGLPGsquareroundsquareroundplaneConvex diamond
Pattern
Concave
Cinquefoil
pattern
Corrugatoin
pattern
Φ 100-280-520--
Φ 110-280-520--
Φ 120-280-520--
Φ 150-280-520--
Φ 80-280-520--
Φ 135-280-520--
Φ 160-280-520--